Fiberglass

Note:
1、Tolerance ranger or OD<1mm, tolerance range of ID<0.5mm
2、Above mentioned sizes are common spcifications, special sizes can be produced according to customers requirement with OD range 32~1300mm and ID range T-1307~130mm.
3、According to customers requirement: plaint wax paper,coating with black paper, coating with non woven fabric waxpaper or with PE.

Technology requirement of the fiberglass
Appearance	Light yellow and black	Volatiles Content	8%--13%
Resin content	28%～34%	Outside Diameter	Φ50～Φ505(mm)
The condition of fiberglass	<25°C	Inside Diameter	Φ7～Φ51(mm)
Relative humidity\|	<75%	Strength	≥0.35(N/Tex)
Ressist pull force(N/50MM)	500～2500

model	（g/㎡) Weight	Tex		Openings/Inch		Tensile/Strength( N/50)		Weave	（Twist)
model	（g/㎡) Weight	Warp	Fill	Warp	Fill	Warp	Fill	Weave	Warp	Fill
CNG160-5*5	160±5%	198*2	400	5±0.5%	5±0.5%	≥1300	≥1300	Leno	105	0
CNG260-5*5	260±5%	330*2	660	5±0.5%	5±0.5%	≥2200	≥2200	Leno	105	0
CNG330-5*5	330±5%	396*2	900	5±0.5%	5±0.5%	≥2450	≥2550	Leno	105	0
CNG380-5*4	380±5%	495*2	1200	5±0.5%	5±0.5%	≥2700	≥2800	Leno	105	0
CNG400-5*4	400±5%	528*2	1200	5±0.5%	5±0.5%	≥2820	≥2800	Leno	105	0
CNG190-6*6	190±5%	198*2	400	6±0.5%	6±0.5%	≥1500	≥1500	Leno	105	0
CNG230-6*6	230±5%	198*2	440	6±0.5%	6±0.5%	≥1500	≥1650	Leno	105	0
CNG85-14*14	85±5%	44*2	66	14±0.5%	14±0.5%	≥800	≥800	Leno	105	0
CNG125-8*8	125±5%	99*2	198	8±0.5%	8±0.5%	≥1000	≥1000	Leno	105	0

NO.	OC	ID	NO.	OC	ID
1	Φ95～Φ98	Φ16.5～Φ17	7	Φ252～Φ254	Φ25.5～Φ26.5
2	Φ110～Φ114	Φ22.5～Φ23	8	Φ295～Φ298	Φ25.5～Φ26.5
3	Φ120～Φ124	Φ22.5～Φ23	9	Φ300～Φ303	Φ25.5～Φ26.5
4	Φ145～Φ148	Φ22.5～Φ23	10	Φ354～Φ349	Φ25.5～Φ26.5
5	Φ175～Φ178	Φ22.5～Φ23	11	Φ350～Φ355	Φ25.5～Φ26.5
6	Φ220～Φ228	Φ22.5～Φ23	12	Φ395～Φ402	Φ30～Φ33

Note:
1、Tolerance ranger or OD<1mm, tolerance range of ID<0.5mm2、Above mentioned sizes are common spcifications, special sizes can be produced according to customers requirement with OD range 32~1300mm and ID range T-1307~130mm.3、According to customers requirement: plaint wax paper,coating with black paper, coating with non woven fabric waxpaper or with PE.